The kinetic competition between transport and oxidation of ferrous ions governs precipitation of corrosion products in carbonated concrete

Authors

  • Matteo Stefanoni Institute for Building Materials, ETH Zurich
  • Zhidong Zhang Institute for Building Materials, ETH Zurich
  • Ueli Angst Institute for Building Materials, ETH Zurich
  • Bernhard Elsener Institute for Building Materials, ETH Zurich and University of Cagliari, Department of Chemical and Geological Science

DOI:

https://doi.org/10.21809/rilemtechlett.2018.57

Abstract

Corrosion products, originating from steel corrosion and precipitating in the concrete pore system, can lead to concrete cracking and to spalling of the concrete cover. Related premature structural repair causes high costs. Thus, reliable quantitative models are needed, which currently do not exist. Here, we present a new conceptual model to describe the fate of ferrous ions that are released at the steel surface during the corrosion process. The key novelty of our approach can be found in explicitly considering the kinetics of oxidation and transport of Fe2+ in the pore solution. These two processes constantly dilute the Fe2+ concentration and are in competition with the supply of Fe2+ from the anodic iron dissolution reaction. We use a numerical model to elucidate which of the described processes is the fastest. The results find good agreement with experimental data and reveal that under natural corrosion conditions, Fe2+ hardly reach the saturation level, which permits the diffusion of corrosion products up to millimeters away from the steel without necessarily leading to expansive stresses. Under accelerated corrosion conditions, however, precipitation is forced immediately at the steel surface. This fundamentally changes the cracking mechanism and questions the relevance of such tests and related models.

The kinetic competition between transport and oxidation of ferrous ions governs precipitation of corrosion products in carbonated concrete

Downloads

Published

14.09.2018

How to Cite

(1)
Stefanoni, M.; Zhang, Z.; Angst, U.; Elsener, B. The Kinetic Competition Between Transport and Oxidation of Ferrous Ions Governs Precipitation of Corrosion Products in Carbonated Concrete. RILEM Tech Lett 2018, 3, 8-16.